SOLOPLAST W2 mold release agent 500ML 393060--VDM

SOLOPLAST W2 500ML release wax

Use: used in thin layers for releasing polyester or epoxy laminate parts from laminate or metal molds.

For application to mold with a cloth before the gel coat. Polishing required.

DESCRIPTION

W2 release wax is a mixture of hard waxes in a chlorine-free solvent used to prevent adhesion between the mold and the part.

W2 release wax forms a hard film and leaves a very slight thickness in the mold.

FIELD OF APPLICATION

Release agent used alone or in thin layers for releasing polyester or epoxy laminate parts from laminate or metal molds.

As a primer for liquid release agents on porous surfaces and surfaces with a complicated surface structure.

Special use as a release agent on submerged molded parts.

Highly effective release agent that ensures a long service life for molds, very economical and easy to work with.

PRODUCT CHARACTERISTICS

Colorless

Liquid consistency

Density at 20°C DIN 51757 0.76 g/ml

Viscosity at 20°C DIN 4 mm beaker < 59 s

Flash point DIN 51755 > 24°C

Drying time 15 to 60 minutes

IMPLEMENTATION

The product must be shaken before and during use and brought to room temperature.

Apply with a soft cloth or air-assisted spray gun. The layer should be thin and even.

Before the first application, the molds must be cleaned with a suitable cleaner.

In a new mold, it is advisable to repeat the application 3 to 4 times.

The solvent must have evaporated between each coat; drying time is 15 to 60 minutes.

The wax film can then be polished. The solvent must have evaporated between applications of the wax.

After about fifty applications of W2 release wax, the mold must be cleaned with a mold cleaner to prevent clogging.

In the event of flocculation, remove by immersing in a bath of hot water at 50°C.

Reference SOLOPLAST: 133754